Abstract: (9328 Views)
In this paper a constitutive equation was considered for the isothermal hot compression test of the Mn-Ni-Cr alloy. The hot compression test was performed in the strain rate range of 0.001-0.1 s-1 and deformation temperature was varied from 700 to 900 °C. A considerable reduction in flow stress was observed regardless of the strain rate when temperature was increased from 700 to 750 °C. DTA and XRD evaluation revealed that the removal of Mn3Cr phase and formation of the single solid solution phase were the reason for the flow stress reduction. At the low deformation temperature (700°C) and the high strain rate (0.1 s-1), a partially recrystallized microstructure was observed; this was such that with increasing the temperature and decreasing the strain rate, a recrystallized microstructure was completed. Also, the relationships between flow stress, strain rate and deformation temperature were addressed by the Zener-Holloman parameter in the exponent type with the hot deformation activation energy of 301.07 KJ/mol. Finally, the constitutive equation was proposed for predicting the flow stress at various strain rates and temperatures.
Full-Text [PDF 1242 kb]
(3430 Downloads)
- The flow stress of the alloy dramatically decreases at 750 ºC
- At low temperature and high strain rate, a partially recrystallized microstructure was observed
- DRX was the dominant softening process at high temperatures and low strain rates
- Hot deformation activation energy of the alloy was 301.07 KJ/mol