A Facile Synthesis of Metallic (Zn and Co) Ferrite nanostructures as Efficient Solid Photocatalysts for Degradation of Methyl Orange and Methyl Blue under Sunlight

Alkhobrani, Salihah; Bayahia, Hossein; Alshorifi, Fares T.

doi:10.22068/ijmse.3284

Volume 20, Issue 3 (September 2023) IJMSE 2023, 20(3): 1-12 | Back to browse issues page

‎ 10.22068/ijmse.3284

Mendeley

Zotero

RefWorks

Alkhobrani S, Bayahia H, Alshorifi F T. A Facile Synthesis of Metallic (Zn and Co) Ferrite nanostructures as Efficient Solid Photocatalysts for Degradation of Methyl Orange and Methyl Blue under Sunlight. IJMSE 2023; 20 (3) :1-12
URL: http://ijmse.iust.ac.ir/article-1-3284-en.html

A Facile Synthesis of Metallic (Zn and Co) Ferrite nanostructures as Efficient Solid Photocatalysts for Degradation of Methyl Orange and Methyl Blue under Sunlight

Salihah Alkhobrani

, Hossein Bayahia

, Fares T. Alshorifi

Abstract: (4355 Views)

In this study, CoFe₂O₄ (CoF) and ZnFe₂O₄ (ZnF) photocatalysts were successfully prepared by a facile and simple chemical precipitation method for degradation of methylene blue (MB) and methyl orange (MO) dyes under direct sunlight irradiation. The obtained ferrites were then characterized through XRD, TEM, EDS, UV-vis, and SEM. XRD and TEM results exhibited cubic nanostructures with sizes ranging from 9 to 16 nm and 11 to 18 nm for ZnF and CoF, respectively. SEM images showed homogenous, porous flat surfaces. EDS spectra confirmed the successful synthesis of ZnF and CoF nanostructures with high purity. UV-vis spectra results of MB and MO dyes showed maximum sunlight absorbance in the absence of ZnF and CoF, whilea regular decrease in the sunlight absorbance was observed in the presence of ZnF and CoFwithin 15-60 min. The UV-vis results also showed that ZnF had higher photocatalytic activity than CoF.The experimental findings showed that the highest % degradation was 92.89% and 96.89% for MO and MB dyes, respectively, over ZnF compared to CoFphotocatalyst (87.55% and 88.41% for MO and MB, respectively). These findings confirm that porous ZnF and CoF nanostructures are critical in promoting the degradation of dyes under sunlight instead of UV-vis light lamps that consume/require electrical energy.

Keywords: Metallic ferrites, CoFe3O4, photocatalysts, methyl orange, ZnFe2O