In this research, samples of AlMg0.7Si aluminum alloy are deformed up to three passes using equal channel angular pressing (ECAP). Formation of a sub-micron structure after three passes of ECAP is demonstrated. Microstructural stability of the samples is investigated at temperatures of 300-500 °C. At 300 °C, fine recrystallized structure forms after 10 min which remains stable when the annealing proceeds up to 18 hrs. However, at 350 °C and higher, the microstructure is quite unstable. Even by 10 sec annealing, the samples exhibit recrystallized structure which turned to abnormal grain growth when temperature enhances to 500 °C and time up to 300 sec.