A. Ahmadi, A. A. Youzbashi, A. Nozad, A. Maghsoudipour, T Ebadzadeh,
Volume 11, Issue 4 (December 2014)
Abstract
Synthesis of YSZ nanopowder by alkoxide sol-gel method, through two different hydrolysis routes, one under careful control by using acetyacetone as ligand, and the other through basic hydrolysis, was investigated. The synthesized powders were characterized by various analytical techniques such as, XRD, STA, PSA, BET, SEM, and TEM. The results showed that, the YSZ powders prepared through the basic hydrolysis route consist of weakly agglomerated nanosized spherical particles whereas the products obtained through the controlled hydrolysis route, consist of hard irregular shaped agglomerates. Sinterability of these powders was examined at 1480 °C, which showed that the powder synthesized through the basic hydrolysis route attains a density of 94%, against 60% for the other case. It was therefore concluded that, alkoxide sol-gel method through basic hydrolysis route, can be more suitable for the synthesis of YSZ nanopowder and its subsequent sintering.
F. Torknik, M. Keyanpour-Rad, A. Maghsoudipour, G. M. Choi,
Volume 13, Issue 1 (March 2016)
Abstract
In order to further enhance the Ni/Ce 0.8Gd0.2O2-δ (Ni/GDC20) cermet anodic performance for low temperature solid oxide fuel cell (LT-SOFC), a study was conducted on the nanostructuring of NiO/GDC composite by only once wet-infiltration of rhodium chloride precursor. By using electrochemical impedance spectroscopy (EIS) analysis, the effect of only one drop of Rh-infiltrating solution on the anodic polarization resistance was examined using symmetric Ni–GDC20|GDC20|Pt electrolyte-supported cell at 400-600 °C. Nanostructural evolution before and after H 2 reduction at 600 °C and also after anodic performance test was investigated by atomic force microscopy (AFM), field emission scanning electron microscopy (FE-SEM), and transmission electron microscopy (TEM) techniques in comparison to the anode itself. Despite the fine distribution of Rh-infiltrated nanoparticles having average particle size of 11.7 nm, the results showed ineffectiveness and inability of the Rh nanoparticles to succeed in decreasing of anodic polarization resistance for H 2 oxidation reaction in LT-SOFC.