Y. Safaei-Naeini, F. Golestani-Fard, F. Khorasanizadeh, M. Aminzare, S. Zhang,
Volume 8, Issue 3 (september 2011 2011)
Abstract

Abstract:

composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at

800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nano

powder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-

Teller (BET) techniques. It was demonstrated that the formation temperature decreased to 850

particles revealed an average size of 30 nm with a narrow size distribution. The mechanism of MgAl

was found to be a template type where the morphology and size of product were similar to those of alumina formed

from boehmite decomposition. Prolonging the reaction time from 0.5 to 3 h, the reaction was further completed and

crystallinity was improved. However, the increase of temperature was more effective in this regard.

MgAl2O4 (MA) nano powder was synthesized via molten salt technique, by heating stochiometric°C. The nano spinel2O4 formation

Page 1 from 1     