Golmahalleh O., Zarei-Hanzaki A.,
Volume 1, Issue 1 (Oct 2004)
Abstract
In principal, a proper combination of strength and ductility is achieved through micro component refinement in steels. This is particularly empowered with ferrite refinement down to micron sizes in ferrite pearlite engineering steels. The latter is achieved through various well-defined methods in which strain induced transformation (SIT) has shown spectacular capabilities. In the present study, to address the effect of thermo mechanical processing parameters on the (SIT) behavior, two plain carbon steels were studied through single pass rolling. This was carried out at the corresponding Ar_3 + 20°C temperature of the steels. The results indicated that the transformation behavior and ferrite morphology would be .strongly influenced by both the chemical composition (i.e., carbon content) and the amount of applied strain. Furthermore, a high volume fraction of very fine ferrite with mean grain size of less than 2 µm was obtained. This was attributed to the ferrite nucleation at deformation bands and serrated austenite grain boundaries.
Fatemi-Varzaneh S.m., Zarei-Hanzaki A.,
Volume 2, Issue 3 (Apr 2005)
Abstract
AZ31 magnesium alloy is considered as a promising alloy in various applications and industries. Furthermore, to design a proper hot working process (rolling, forging and extrusion), the assessment of hot working behaviour of the alloy is necessary. Accordingly, the hot deformation behaviour of AZ31 alloy was studied through hot compression testing method This was carried out in a wide range of temperature (523K to 783K) and strain rates. The obtained true stress-true strain curves and final microstructures were examined and a partial melting was realized at 740K. It was concluded that the presence of liquid did change the deformation mechanisms thereby affecting the flow behaviour.