Ghobeiti Hasab M., Seyyed Ebrahimi S.a., Badaee A.,
Volume 2, Issue 2 (6-2005)
Abstract
In this research the sol-gel auto-combustion method was used to prepare strontium hexaferrite nanopowder. A solution of distilled water, ferric and strontium nitrates, citric acid, trimethylamine, and n-decyltrimethylammonium bromide cationic surfactant, was heated to form a viscous gel. The gel was heated and then ignited automatically. As-burnt powder was calcined at temperatures from 700 to 900?C in air to obtain SrO.6Fe2O3 phase. The influence of the calcination temperature on the phase composition of the products has been investigated. X-ray diffraction confirmed the formation of single-phase strontium hexaferrite nanopowder at temperature of 800?C.
A. Allahverdi, Z. Padar, M. Mahinroosta,
Volume 16, Issue 2 (6-2019)
Abstract
It is demonstrated that the addition of organo-modified Na-bentonite (OMB) particles to Portland cement mortar can promote its physical and mechanical properties. A series of experimental works on some important physico-mechanical properties of Portland cement mortars mixed with various dosages of hydrophobic OMB were performed. The obtained results confirm that the OMB provides a dense packing effect. An optimum replacement level of around 3.5% (by weight) at an increased water-to-cement ratio of 0.53 results in an almost 11.43% increase in 28-day compressive strength along with about 20.78 and 16.20% reductions in total volume of permeable pore space and water absorption, respectively. Also, at the optimum replacement level, an increase of about 2.72% is taken place in dry bulk specific gravity.