P. Amin, A. Nourbakhsh, P. Asgarian, R. Ebrahimi Kahrizsangi,
Volume 13, Issue 3 (9-2016)
Abstract
In this study, Boron carbide was synthesized using Mesoporous Carbon CMK-1, Boron oxide, and magnesiothermic reduction process. The Effects of temperature and magnesium grain size on the formation of boron carbide were studied using nano composite precurser containg mesoporous carbon. Samples were leached in 2M Hydrochloric acid to separate Mg, MgO and magnesium-borat phases. SEM, XRD and Xray map analysis were caried out on the leached samples to characterize the boron carbide. results showed that the reaction efficiency developed in samples with weight ratio of B2O3:C:Mg = 11:1.5:12, by increasing the temperature from 550 to 650 °C and magnesium powder size from 0.3 m to 3 m.
Gholam Hussein Borhani, Saeed Reza Bakhshi, Sadegh Soltani,
Volume 18, Issue 2 (6-2021)
Abstract
In this study, Ta powder was produced from Ta scarp via chemical processes using Mg and Ca powders. At first, Tantalum scraps were converted to Tantalum oxide (Ta2O5) at 1100˚C in an oxygen atmosphere. Tantalum oxide was reduced to Tantalum powder with Mg in a vacuum environment at 950 to 1200˚C for 3 hours. The obtained Ta powders further were reacted with Ca at 950˚C for 5 hours in a vacuum atmosphere. The powders were analyzed through X-ray diffraction patterns (XRD), scanning electron microscopy (SEM), as well as oxygen measurement. The results show that the average particles size of the produced Ta powders is about 58 nm with oxygen contents of 250 ppm.